This document provides information on tuning the "pressure advance"
|
|
configuration variables for a particular nozzle and filament. The
|
|
pressure advance feature can be helpful in reducing ooze. For more
|
|
information on how pressure advance is implemented see the
|
|
[kinematics](Kinematics.md) document.
|
|
|
|
Prerequisites
|
|
=============
|
|
|
|
In order to tune the pressure advance setting the printer must be
|
|
configured and operational. The tuning test involves printing objects
|
|
and inspecting the differences between objects. In particular, the
|
|
extruder
|
|
[E steps](http://reprap.org/wiki/Triffid_Hunter%27s_Calibration_Guide#E_steps)
|
|
and
|
|
[nozzle temperature](http://reprap.org/wiki/Triffid_Hunter%27s_Calibration_Guide#Nozzle_Temperature)
|
|
should be tuned prior to tuning pressure advance.
|
|
|
|
Tuning pressure advance
|
|
=======================
|
|
|
|
Pressure advance does two useful things - it reduces ooze during
|
|
non-extrude moves and it reduces blobbing during cornering. This guide
|
|
uses the second feature (reducing blobbing during cornering) as a
|
|
mechanism for measuring and tuning the pressure advance configuration.
|
|
|
|
Start by changing the extruder section of the config file so that
|
|
pressure_advance is set to 0.0. (Make sure to issue a RESTART command
|
|
after each update to the config file so that the new configuration
|
|
takes effect.) Then print at least 10 layers of a large hollow square
|
|
at high speed (eg, 100mm/s). See
|
|
[docs/prints/square.stl](prints/square.stl) file for an STL file that
|
|
one may use. While the object is printing, make a note of which
|
|
direction the head is moving during external perimeters. What many
|
|
people see here is blobbing occurring at the corners - extra filament
|
|
at the corner in the direction the head travels followed by a possible
|
|
lack of filament on the side immediately after that corner:
|
|
|
|
|
|
|
|
This blobbing is the result of pressure in the extruder being released
|
|
as a blob when the head slows down to corner.
|
|
|
|
The next step is to set pressure_advance_lookahead_time to 0.0, slowly
|
|
increase pressure_advance (eg, start with 0.05), and reprint the test
|
|
object. (Be sure to issue RESTART between each config change.) The
|
|
goal is to attempt to eliminate the blobbing during cornering. (With
|
|
pressure advance, the extruder will retract when the head slows down,
|
|
thus countering the pressure buildup and ideally eliminate the
|
|
blobbing.)
|
|
|
|
If a test run is done with a pressure_advance setting that is too
|
|
high, one typically sees a dimple in the corner followed by possible
|
|
blobbing after the corner (too much filament is retracted during slow
|
|
down and then too much filament is extruded during the following speed
|
|
up after cornering):
|
|
|
|
|
|
|
|
The goal is to find the smallest pressure_advance value that results
|
|
in good quality corners:
|
|
|
|
|
|
|
|
Typical pressure_advance values are between 0.05 and 0.20 (the high
|
|
end usually only with bowden extruders). If there is no significant
|
|
improvement seen after increasing pressure_advance to 0.20, then
|
|
pressure advance is unlikely to improve the quality of prints. Return
|
|
to a default configuration with pressure_advance disabled.
|
|
|
|
It is not unusual for one corner of the test print to be consistently
|
|
different than the other three corners. This typically occurs when the
|
|
slicer arranges to always change Z height at that corner. If this
|
|
occurs, then ignore that corner and tune pressure_advance using the
|
|
other three corners.
|
|
|
|
Once a good pressure_advance value is found, return
|
|
pressure_advance_lookahead_time to its default (0.010). This parameter
|
|
controls how far in advance to check if a head slow-down is
|
|
immediately followed by a speed-up - it reduces pointless pressure
|
|
changes in the head. It's possible to tune this - higher values will
|
|
decrease the number of pressure changes in the nozzle at the expense
|
|
of permitting more blobbing during cornering. (Tuning this value is
|
|
unlikely to impact ooze.) The default of 10ms should work well on most
|
|
printers.
|
|
|
|
Although this tuning exercise directly improves the quality of
|
|
corners, it's worth remembering that a good pressure advance
|
|
configuration can reduce ooze throughout the print.
|
|
|
|
Finally, once pressure_advance is tuned in Klipper, it may still be
|
|
useful to configure a small retract value in the slicer (eg, 0.75mm)
|
|
and to utilize the slicer's "wipe on retract option" if available.
|
|
These slicer settings may help counteract ooze caused by filament
|
|
cohesion (filament pulled out of the nozzle due to the stickiness of
|
|
the plastic). It is recommended to disable the slicer's "z-lift on
|
|
retract" option.
|